Conventional materials necessitate a layer-by-layer rolling or tamping process for subgrade backfill projects, which hampers their utility in confined spaces and environments where compaction is challenging. To address this issue, a self-compacting poured solidified mucky soil was prepared. To assess the suitability of this innovative material for subgrade, a suite of performance including flowability, bleeding rate, setting time, unconfined compressive strength (UCS), and deformation modulus were employed as evaluation criteria. The workability and mechanical properties of poured solidified mucky soil were compared. The durability and solidification mechanism were investigated. The results demonstrate that the 28-day UCS of poured solidified mucky soil with 20% curing agent content reaches 2.54 MPa. The increase of organic matter content is not conducive to the solidification process. When the curing temperature is 20 degrees C, the 28-day UCS of the poured solidified mucky soil with curing agent content not less than 12% is greater than 0.8 MPa. The three-dimensional network structure formed with calcium silicate hydrate, calcium aluminate hydrate, and ettringite is the main source of strength formation. The recommended mud moisture content is not exceed 85%, the curing agent content is 16%, and the curing temperature should not be lower than 20 degrees C.

On December 18, 2023, a magnitude MS6.2 earthquake struck Jishishan County, Gansu Province, triggering over 40 seismic subsidence sites within a seismic intensity VI zone, 32 km from the epicenter.The earthquake caused tens of millions in economic losses to mountain photovoltaic power stations. Extensive geological surveys and comparisons with similar landslides (such as soil loosening, widespread cracks, and stepped displacements) triggered by the 1920 Haiyuan MS8.5 earthquake and the 1995 Yongdeng MS5.8 earthquake, this study preliminarily identifies one subsidence sites as a seismic-collapsed loess landslide. To investigate its disaster-causing mechanism: the dynamic triaxial test was conducted to assess the seismic subsidence potential of the loess at the site, and the maximum subsidence amount under different seismic loads were calculated by combining actual data from nearby bedrock stations with site amplification data from the active source; simulation of the destabilization evolution of seismic-collapsed loess landslides by large-scale shaking table tests; and a three-dimensional slope model was developed using finite element method to study the complex seismic conditions responsible for site damage. The research findings provide a theoretical foundation for further investigations into the disaster mechanisms of seismic-collapsed loess landslides.

To investigate the effect of interface temperature on the soil-reinforcement interaction mechanism, a series of pullout tests were conducted considering different types of reinforcement (geogrid and non-woven geotextile), backfill (dry sand, wet sand, and clay), and six interface temperatures. The test results indicate that at interface temperatures of 0 degrees C and above, reinforcement failure didn't occur during the pullout tests, whereas it predominantly occurred at subzero temperatures. Besides, the pullout resistance for the same soil-reinforcement interface gradually decreased as the interface temperature rose. At a given positive interface temperature, the pullout resistance between wet sand and reinforcement was significantly higher than that of the clayreinforcement interface but lower than that of the dry sand-reinforcement interface. Compared with geotextile reinforcements, geogrids were more difficult to pull out under the same interface temperature and backfill conditions. In addition, the lag effect in the transfer of tensile forces within the reinforcements was significantly influenced by the type of soil-reinforcement interface and the interface temperature. Finally, the progressive deformation mechanism along the reinforcement length at different interface temperatures was analyzed based on the strain distribution in the reinforcement.

To investigate the coupled time effects of root reinforcement and wet-dry deterioration in herbaceous plant-loess composites, as well as their microscopic mechanisms, this study focused on alfalfa root-loess composites at different growth stages cultivated under controlled conditions. The research included measuring root morphological parameters, conducting wet-dry cycling tests, and performing triaxial compression tests and microscopic analyses (CT scanning and nuclear magnetic resonance) on both bare loess and root-loess composites under various wet-dry cycling conditions. By obtaining shear strength parameters and microstructural indices, the study analyzed the temporal evolution of the shear strength and microstructural characteristics of root-loess composites under wet-dry cycling. The findings indicated that the alfalfa root-loess composite effective cohesion was significantly higher than that of the plain soil in the same growth stage. The alfalfa root-loess composite effective cohesion increased during the growth stage in the same dry-wet cycles. The alfalfa root-loess composite effective cohesion in the same growth stage was negatively correlated with the number of dry-wet cycles. The fatigue damage of the soil's microstructure (pore coarsening, cement hydrolysis, and crack development) increased continuously with the number of dry-wet cycles. However, due to the difference in mechanical properties between roots and the soil, the root-soil composite prevented the deterioration of the soil matrix strength by the dry-wet cycles. As the herbaceous plants grow, the time effect observed in the shear strength of the root-soil composite under the action of dry-wet cycles is the result of the interaction and dynamic coordination between the soil-stabilizing function of the herbaceous plant roots and the deterioration caused by drywet cycles.

Post-grouting pile technology has gained extensive application in collapsible loess regions through the injection of slurry to compress and consolidate the soil at the pile base, thereby forming an enlarged base that enhances the foundation's bearing capacity and reduces settlement. Despite the prevalent unsaturated state of loess in most scenarios, the conventional design methodologies for piles in collapsible loess predominantly rely on saturated soil mechanics principles. The infiltration of water can significantly deteriorate the mechanical properties of loess due to the reduction in matric suction and the occurrence of collapsible deformation, leading to a substantial degradation in the bearing behavior of piles. To explore the variations in load transfer mechanisms of post-grouting piles in collapsible loess under conditions of intense precipitation, a comprehensive large-scale model test was conducted. The findings revealed that the post-grouting technique effectively mitigates the adverse effects of negative pile shaft friction in saturated zones on the pile's bearing behavior. Furthermore, the failure criteria for piles may shift from the shear failure of the base soil to excessive pile settlement. By incorporating principles of unsaturated soil mechanics, modified load transfer curves were developed to describe the mobilization of both pile shaft friction and base resistance. These curves facilitate the extension of the traditional load transfer method to post-grouting piles in collapsible soils under extreme weather conditions. The proposed revised load transfer method is characterized by its simplicity, requiring only a few soil indices and mechanical properties, making it highly applicable in engineering practice.

This study investigates the microhardness and geometric degradation mechanisms of interfacial transition zones (ITZs) in recycled aggregate concrete (RAC) exposed to saline soil attack, focusing on the influence of supplementary cementitious materials (SCMs). Ten RAC mixtures incorporating fly ash (FA), granulated blast furnace slag (GBFS), silica fume (SF), and metakaolin (MK) at 10 %, 15 %, and 20 % replacement ratios were subjected to 180 dry-wet cycles in a 7.5 %MgSO4-7.5 %Na2SO4-5 %NaCl solution. Key results reveal that ITZ's microhardness and geometric degradation decreases with exposure depth but intensifies with prolonged dry-wet cycles. The FAGBFS synergistically enhances ITZ microhardness while minimizing geometric deterioration, with ITZ's width and porosity reduced to 67.6-69.0 mu m and 25.83 %, respectively. In contrast, FA-SF and FA-MK exacerbate microhardness degradation, increasing porosity and amplifying microcrack coalescence. FA-GBFS mitigates the diffusion-leaching of aggressive/original ions and suppresses the formation of corrosion products, thereby inhibiting the initiation and propagation of microcracks. In contrast, FA-SF and FA-MK promote the formation of ettringite/gypsum and crystallization bloedite/glauberite, which facilitates the formation of trunk-limb-twig cracks.

Silica fume and carbide slag can be used to modify waste mud soil (WMS), which can not only improve the mechanical properties of WMS, but also broaden resource utilization ways of silica fume and carbide slag. For that, in this paper, WMS was modified by adopting 8 % carbide slag and silica fume with different dosages (0, 3 %, 5 %, 7 %, 9 %, and 11 %). Then the small-strain dynamic properties of modified WMS were investigated by using resonance column test, and the microscopic mechanism of modified WMS was analyzed based on Scanning electron microscopy (SEM), Energy dispersive X-ray spectrometer (EDS), Transmission electron microscopy (TEM), X-ray diffraction test (XRD) and Mercury intrusion porosimetry (MIP). It can be found from the resonance column test that the dynamic shear modulus and the damping ratio show an increasing and decreasing trend with the increase of the confining pressure respectively, and both increase with increasing silica fume dosage in the range of 0 to 11 %. A kinetic model applicable to modified WMS was established by introducing the effects of confining pressure and silica fume into the Hardin-Drnevich model. Microscopic testing experiments indicate that there is a reaction between reactive SiO2 in silica fume and Ca(OH)2 in carbide slag, and calcium hydrated silicate (CSH) was generated, which improved the specimen density.

This paper proposes a carbon fiber reinforced polymer (CFRP) retrofitting scheme for improving the seismic performance of atrium-style metro stations (AMS). Past experimental studies have confirmed that the weakest of the AMS during strong earthquakes is located at the upper-story beam ends. However, there is thus far no candidate for a reference approach to retrofitting and strengthening the AMS. This study addresses this gap by applying CFRP retrofitting to both ends of the upper-story beam. The main objective is to assess the effectiveness of the proposed retrofitting scheme. First, a three-dimensional finite element model is developed to simulate dynamic soil-AMS interaction. The validity of the numerical method is assessed via a comparison with measured data from reduced-scale model tests. Second, a numerical model of the AMS retrofitted with CFRP is built using validated methods. Finally, dynamic time-history analyses of the AMS with and without CFRP retrofitting are conducted, and their dynamic responses, including inter-story drift, dynamic strain, and tensile damage, in conjunction with the lateral displacement of the surrounding ground, are compared. Comparison of the results for the non-retrofitted and retrofitted structures shows that CFRP retrofitting significantly reduces both the principal strains and tensile damage factors at the upper-story beam ends while slightly increasing those values at the mid-span of the beam; additionally, it does not change the structural lateral deformation. Therefore, it can be concluded that CFRP retrofitting could effectively improve the seismic performance of the AMS without changing its lateral stiffness.

The hysteresis effect of unfrozen water during freeze-thaw cycles greatly influences the hydrothermal properties of soil. To better understand the hysteresis behavior of unfrozen water in the soil, this study utilized frequency domain reflectometry to measure the unfrozen water content variations in silty clay under both stepwise and rapid temperature change modes. The hysteresis effect of unfrozen water in soil was analyzed, also the underlying mechanism was revealed. The results indicate that unfrozen water content variations are consistent across the two temperature change modes, with hysteresis observed in both scenarios. This effect was more noticeable during the rapid temperature change mode, and soil samples with higher initial moisture content froze earlier and thawed more slowly in this mode. The hysteresis phenomena are mainly influenced by the ice crystal metastable nucleation, the blockage effect of pore ice crystallization, and the pore water pressure changes during phase transition. The main cause of unfrozen water hysteresis in soil during the initial freezing phase is the metastable nucleation process. In the later stages of freezing, the hysteresis effect is primarily driven by changes in capillary water curvature, induced by the blockage effect of pore ice crystallization, and shifts in pore water pressure during the ice-water phase transition. Also, a hysteresis model was proposed and validated against experimental data and existing models, demonstrating good performance and accurately predicting unfrozen water content under varying temperature conditions. This research enhances the understanding of the mechanism responsible for the hysteresis effect of unfrozen water content in frozen soil.

Seasonal freezing and thawing significantly influence the migration and distribution of soil hydrothermal salts. Understanding the dynamics of hydrothermal salt forces in canal foundation soils is crucial for effective canal disease control and optimization. However, the impact on rectangular canals remains poorly understood. Therefore, field-scale studies on water-heat-salt-force-displacement monitoring were conducted for the canal. The study analyzed the changes and interaction mechanisms of water-heat-salt-force in the soil beneath the canal, along with the damage mechanisms and preventive measures. The results indicate that the most rapid changes in temperature, moisture, and salt occur in the subsoil on the canal side, with the greatest depth of freezing. Heat transfer efficiency provides an intuitive explanation for the sensitivity of ground temperature at the junction of the canal wall and subsoil to air temperature fluctuations, as well as the minimal moisture migration in this region under the subcooling effect. The temperature-moisture curve suggests that current waterheat-force and water-heat-salt-force models exhibit a delay in accurately predicting water migration within the subsoil. Rectangular canals are more susceptible to damage under peak freezing conditions, requiring a combined approach of freezing restraint and frost-heaving force to mitigate damage. These findings offer valuable insights for canal design, maintenance, and further research.