Keratin waste has become an increasingly serious environmental and health hazard. Keratin waste is mainly composed of keratin protein, which is one of the most difficult polymers to break down in nature and is resistant to many physical, chemical, and biological agents. With physical and chemical methods being environment damaging and costly, microbial degradation of keratin using keratinase enzyme is of great significance as it is both environment friendly and costeffective. The aim of this study was to extract and purify keratinase from bacterial species isolated from the soil. Among the organisms, an isolate of Bacillus velezensis, coded as MAMA could break down chicken feathers within 72 hours (h). The isolated strain produced significant levels of keratinase in mineral salt medium by supplying chicken feathers as the sole source of nitrogen and carbon. Feather deterioration was observed with the naked eye, and enzyme activity was evaluated using a spectrophotometric assay. Sodium dodecyl-sulfate polyacrylamide gel electrophoresis (SDS-PAGE) and zymography results revealed that the keratinase protein produced by Bacillus velezensis had a molecular weight between 40 and 55 kilodalton (kDa).

In this paper glass/chicken feathers reinforced epoxy composite and glass/chicken feathers reinforced polyester composite was prepared in the laboratory at different percentage of the glass and chicken feathers. Tensile properties, flexural properties, shore hardness and impact strength of the glass/chicken feathers reinforced epoxy composite and glass/chicken feathers reinforced polyester composite was studied experimentally and compared at different percentage of the glass and chicken feathers. The composite will be used in humid and corrosive environment; therefore, water absorption and acid corrosion test were performed. To understand the degradation behaviour of the composite, soil test was performed. Scanning electron microscopy analysis was carried out to find the fracture and interfacial characteristics of the composites after tensile test. This hybrid composite can be used in automobile, structural and defense sector. Glass/chicken feathers reinforced epoxy composite and glass/chicken feathers reinforced polyester composite plate was prepared in the laboratory at different percentage of the glass and chicken feathers. Tensile properties and shore hardness of each composite was studied experimentally and compared at different percentage of the glass and chicken feathers. image

Keratin was synthesized by alkaline hydrolysis from chicken feathers and then continue by casting method for producing bioplastics with additional various amounts of chitosan as a filler, polyvinyl alcohol (PVA) and glycerol as a plasticizer. The main purpose is analysis the effect of chitosan on the structural properties using quantitative analysis of X-ray diffraction (XRD) spectra, chemical bonding by Fourier transforms infrared (FTIR) spectra, and mechanical properties by texture analyser to the keratin-based bioplastics. Biodegradation of bioplastics was analysed from the loss of weight by burying in the soil. It's found that, the additional of chitosan (0 %, 2 %, 5 %, and 8 %) increased the crystallinity of bioplastics by 11.83 %, 11.12 %, 18.99 %, and 17.03 %, respectively, but decreasing tensile strength and elasticity of bioplastics. Degradation of bioplastic keratin-based shows that the addition of chitosan can reduce the degradation time which is directly proportional to the loss of C -- O bonds. The highest degradation rate is 89.29 % in 49 days for keratin-based bioplastics with 8 % chitosan, indicated that high potential for future production.