The large-scale development of urban underground spaces has resulted in hundreds of millions of cubic meters of accumulated shield soil dreg waste, occupying huge amounts of land resources and potentially causing groundwater pollution and soil salinization. In this study, shield soil dreg waste is recycled and activated to substitute cement in ultra-high performance concrete, aiming to promote solid waste management and sustainable construction. The slump, mechanical performance, and autogenous shrinkage of the concrete are investigated through macro-scale tests, and the underlying mechanism is revealed via micro-scale experiments. The incorporation of calcined shield soil dreg reduces flowability and leads to a 10.2 % deterioration in compressive strength of the ultra-high performance concrete while mitigating autogenous shrinkage. The primary reason is due to the low CaO content of shield soil dreg, which limits the formation of calcium silicate hydrate, and its high SiO2/Al2O3 content slows hydration kinetics. The environmental and economic benefits of the concrete are determined via life cycle analysis. Recycling shield soil dreg waste into concrete results in about 35 % reduction in carbon emission and 22 % reduction in energy consumption. According to multi-criteria assessment, the overall performance of the concrete considering economic cost, environmental benefit, as well as physical and mechanical properties increases compared to the pristine concrete, achieving well-balanced economic feasibility, environmental sustainability, and engineering performance. The findings of this study provide an effective approach for recycling shield soil dreg and preparing low-carbon concrete, thus promoting solid waste management and sustainable construction.

Biogrouting, a method to enhance soil properties using microorganisms and mechanical techniques, has shown great potential for soil improvement. Most studies focus on small sand columns in labs, but recent tests used 0.5 m plastic boxes filled with sand stabilized with microorganisms and fly ash. The experiments, conducted over 30 days, applied injection and infusion methods with microbial fluids, maintaining groundwater levels to simulate field conditions. Mechanical properties were analyzed through unconfined compressive strength (UCS) tests on extracted samples. Researchers also assessed calcium carbonate distribution and shear strength. Results showed water saturation significantly influenced vertical stress (qu), while UCS correlated with the permeability of sand containing varying calcium carbonate levels. Bacillus safensis, a resilient bacterium used in this process, can withstand extreme conditions. After completing its task, it enters a dormant state and reactivates when needed. The bacteria produce calcium carbonate by binding calcium with enzymes, which cements soil particles, enhancing strength and stability. center dot Testing enzymes on microbes and natural soil center dot Installation settings for drip tools using infusion center dot Soil resistance testing after stabilization using UCS

In response to the environmental challenges posed by conventional expansive soil stabilization methods, this study investigates the low-carbon potential of industrial by-products-cement kiln dust (CKD) and calcium carbide slag (CCS)-as sustainable stabilizers. A comprehensive series of laboratory tests, including compaction tests, free swelling rate measurements, unconfined compressive strength (UCS) evaluations, and scanning electron microscopy (SEM) analyses, were conducted on expansive soil samples treated with varying dosages in both single and binary formulations. The results indicate that the binary system significantly outperforms individual stabilizers; for example, a formulation containing 10% CKD and 9% CCS achieved a maximum dry density of 1.64 g/cm3, reduced the free swelling rate to 22.7% at 28 days, and reached a UCS of 371.3 kPa. SEM analysis further revealed that the enhanced performance is due to the synergistic formation of hydration products-namely calcium silicate hydrate (C-S-H) and calcium aluminate hydrate (C-A-H)-which effectively fill interparticle voids and reinforce soil structure. These findings demonstrate that the dual mechanism, combining rapid early-stage hydration from CCS with sustained long-term strength development from CKD, offers a cost-effective and environmentally sustainable alternative to traditional stabilizers for expansive soils.

This study investigates the sustainable use of seabed dredged sediments and water treatment sludges as construction materials using combined dewatering and cement stabilization techniques. Dredged sediments and water treatment sludges, typically considered waste, were evaluated for their suitability in construction through a series of dewatering and stabilization processes. Dewatering significantly reduced the initial moisture content, while cement stabilization improved the mechanical properties, including strength and stiffness. The unconfined compressive strength (UCS), shear modulus, and microstructural changes were evaluated using various analytical techniques, including unconfined compression testing, free-free resonance testing, X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDX). The results show a direct correlation between reduced w/c ratios and increased UCS, confirming the potential of treated sludge as a subbase layer for roads and landfill liners. A chemical analysis revealed the formation of calcium silicate hydrate (CSH) and ettringite, which are critical for strength enhancement. This approach not only mitigates the environmental issues associated with sludge disposal but also supports sustainable construction practices by reusing waste materials. This study concludes that cement-stabilized dredged sediments and water treatment sludges provide an environmentally friendly and effective alternative for use in civil engineering projects.

The rising demand for housing, propelled by population growth, calls for affordable and reliable construction materials. Compressed Stabilized Earth Blocks (CSEB), an environmentally friendly construction material, serves as a potential solution. The clay soil retrieved from the Olifantsfontein Resource Facility, previously unused and occupying valuable space, was repurposed to produce CSEB, aligning with the company's waste reduction commitment. Soil analysis following South African National Standards (SANS) and American Society for Testing and Materials (ASTM) guidelines, revealing poorly graded sand with silt and clay. River sand was chosen based on particle packing theory to achieve a well graded PSD. Three mixtures with varying clay and river sand proportions, while maintaining a constant cement content of 5%, were prepared. Optimum moisture content was determined through trials with different moisture levels. A compressive strength test, both dry and wet, along with a water absorption test, were conducted to evaluate the brick's performance under variable conditions. Results showed that increasing clay content improved compressive strength, classifying the bricks as load-bearing. The study's compressive strength test results ranged between 3-5 MPa, with dry compressive strength outperforming wet compressive strength. On average, the three mixtures exhibited a water absorption of 11.31%, although mix designs with varying clay content showed different average water contents due to the water-absorption properties of cement and the water-holding capacity of clay. Overall, the findings demonstrate the potential of Olifantsfontein clay as a sustainable construction material for meeting the increasing demand for housing.

Concrete is widely used in civil engineering applications and the natural aggregates which used in concrete are scarce, but its demand is increasing. The disposal of rubber tyres poses a significant environmental challenge, as their decomposition releases harmful chemicals into the soil and water bodies over many years. Decomposition of tyres should be done in a smart way and hence came the emergence of mixing recycled rubber crumbs into concrete as Rubberised Concrete (RC). This paper provides an in-depth analysis of the mechanical properties of concrete such as Compressive Strength (fck), Tensile Strength (ft), Flexural Strength (fcr) of 7, 14, 28 days in replacement of fine aggregate with fine rubber (FR), and Coarse Aggregate with Coarse Rubber (CR). The results indicate that RC is more suitable for structural applications, including Reinforced Concrete columns, beams, slabs, than conventional concrete. The primary objective of the article is to explore the potential use of recycled rubber crumbs in concrete, referred to as Rubberised Concrete (RC), and to analyze its mechanical properties such as compressive strength, tensile strength, and flexural strength over different curing periods. Additionally, machine learning (ML) based prediction model has been developed for various strength characteristics of concrete mixtures at 28 days. The hyperparameter optimization using Grid Search CV with fivefold cross-validation have been performed to obtain the best hyperparameters. The model's performance is evaluated using metrics like MAE, MSE, RMSE, and R-squared values. Results reveal varying performances among different ML algorithms for predicting flexural, tensile, and compressive strengths.

Nowadays, for soil stabilisation and cleaner production of geo-composites, the possibility of utilizing waste rubber is in vogue. The present paper deals with experimentally investigating the mechanical and microstructural characteristics of weak Indian clayey soil partially substituted with lime (0-3.5%) and waste rubber tyre powder (0-15%). It was observed that, with increasing lime and rubber powder content, the plasticity index of the soil decreases. The shear strength and compaction testing results reveal that adding lime and rubber tyre powder (RTP) enhances the geotechnical performance of clayey soil up to an optimum dosage value. Also, the triaxial shear testing was performed to obtain stress-strain curves for all considered soil mixes. For modified clayey soil containing 3% lime and 12.5% rubber powder, the cohesion values and bearing capacities improved phenomenally by 36.1% and 88.6% respectively, when compared to clayey soil. Further for this mix, SEM analysis reveals a compacted microstructure which improves dry-density and California's bearing ratio among all modified mixes. The novel co-relations upon regression analysis are found able to predict plasticity index, dry density, bearing capacity and shear strength with higher confidence levels. Overall, the cost-benefit analysis worked out to obtain the optimum cost of construction of footings and flexible pavement shows cost deductions up to 19% and 39% respectively while utilizing modified clay soil mixes containing 3% lime and 12.5% rubber powder in subgrade, ultimately making production stronger, cheaper and environment friendly.

This article investigates the hygrothermal properties of earth-based materials by analyzing experimental data from 88 articles spanning 32 countries worldwide. The focus is determining effective techniques for leveraging the use of excavated soil in construction, particularly emphasizing enhancement of hygrothermal comfort in specific climates. Based on statistical analysis, the study presents a comprehensive classification of earth production techniques, incorporating additives, and examines their impacts on hygrothermal properties of excavated soils. Additionally, it explores the intricate relationship between the climatic conditions of a region and the chosen earth-material production techniques. The analysis aims to propose standard parameters for earthen materials and identify gaps in both methods and experimental studies. Therefore, this study will provide valuable insights by proposing new design tools (ternary diagrams) to maximize the use of excavated soils in construction practices. The proposed diagrams illustrate the intricate relation linking either hygrothermal properties, the climate zone, and manufacturing techniques, or the relation between the most studied manufacturing techniques (compaction, fibered, and stabilization) and expected dry thermal conductivity. Thereby, results from this meta-analysis and critical review will contribute to advancing sustainable construction practices.

Searching for alternative material options to reduce the extraction of natural resources is essential for promoting a more sustainable world. This is especially relevant in construction and infrastructure projects, where significant volumes of materials are used. This paper aims to introduce three alternative materials, crushed ground glass (GG), recycled gypsum (GY) and crushed lime waste (CLW), byproducts of construction industry geomaterials, to enhance the mechanical properties of clay soil in Cartagena de Indias, Colombia. These materials show promise as cementitious and frictional agents, combined with soil and cement. Rigorous testing, including tests on unconfined compressive strength (qu) and initial stiffness (Go) and with a scanning electron microscope (SEM), reveals a correlation between strength, stiffness and the novel porosity/binder index (eta/Civ) and provides mixed design equations for the novel geomaterials. Micro-level analyses show the formation of hydrated calcium silicates and complex interactions among the waste materials, cement and clay. These new geomaterials offer an eco-friendly alternative to traditional cementation, contributing to geotechnical solutions in vulnerable tropical regions.