The purpose of this study was to evaluate the sustainability benefits of Class F fly ash (FA), lime sludge (LS), and ground granulated blast furnace slag (GGBS)-based geopolymer-stabilized Edgar plastic kaolin (EPK) clay using the sustainability index (ISus) approach. Geotechnical engineering operations usually precede most infrastructural projects, making pavement construction an integral contributor to various environmental effects, due to the production of enormous quantities of greenhouse gas emissions through soil stabilization activities. To nip these concerns in the bud, effective integration of these environmental implications must be achieved during the geotechnical planning phase. The life cycle assessment (LCA) method was used to assess a wide range of environmental effects of a project, from raw material procurement, manufacturing, transportation, construction, and maintenance to final disposal. It is a well-recognized tool for designing environmentally sustainable projects. Experimental results from the geopolymer-stabilized EPK clay showed a notable improvement in unconfined compressive strength of the geopolymer-stabilized clay with 15% (FA + LS) and 5% (FA + GGBS) contents of up to 697% and 464%, respectively, after 28 days of curing at elevated temperature, 70 degrees C. The sustainability index (ISus) of geopolymer and lime treatment methods was analyzed based on the concept of environmental, resource consumption, and socioeconomic concerns, which quantifies the sustainability through greenhouse gas emission, environmental impacts, and the cost of utilizing FA, LS, and GGBS in soil stabilization compared with traditional lime. LCA was conducted for traditional lime treatment, FA-LS, and FA-GGBS geopolymer-stabilized subgrades to determine the most sustainable treatment method. From the sustainability analysis, using FA, LS, and GGBS as geopolymer stabilizers for kaolin clay reduced the global warming potential by 98.03% and 77.55% over the traditional lime stabilizers at 8% dosage. More importantly, results from the sustainability index (ISus) computations showed that FA-LS (ISus = 12.88) and FA-GGBS (ISus = 29.72) geopolymer treatment methods of EPK clay subgrade soils are more sustainable alternatives compared to the traditional lime (ISus = 48.07) treatment method.

Undrained behavior of sandy soil with fines content is a challenge in geotechnical research. In this article, the effect of low clay content (plastic Kaolin) on the anisotropic behavior of sand is studied. In the technical literature, there are different data about the effect of fine particles (generally high percentage), but there are not enough studies on low fines content (especially plastic fines) and anisotropic conditions. For this purpose, 30 undrained tests are performed using a torsional shear hollow cylindrical apparatus (TSHCA) with constant (alpha o) and (b) values on Firoozkuh sand. The specimens had Kaolin contents of 0, 3, 5, 7 and 10%, and the inclination angle (alpha o) is varied from 15o to 60o. The specimens are prepared by dry deposition method and are consolidated under P'c= 100 and 200 kPa. The results of the experiments show that increasing the (alpha o) leads to more contractive behavior in sand. By adding clay particles to the host sand up to 3%, the peak strength of the specimen is increased (7% and 6% for alpha=15 degrees and 30 degrees, respectively), and then with the increase of clay content up to 10%, the strength of the specimen is decreased (33% and 22% for alpha=15 degrees and 30 degrees, respectively). But at alpha = 60o, with the addition of 5% clay, decrease in the peak strength is observed (about 15%) and with a further increase in the clay content, unlike the angles of 15o and 30o, increase in the peak strength of the specimen is observed, so that at 10% clay, the strength of the specimen is higher than the host sand (about 7%), which can be attributed to the cohesion nature of the clay particles. With the increase of clay content, anisotropy degree is decreased. In other words, with the increase of fines content, the anisotropic behavior is decreased.