Geopolymers are recently recognized as superior sustainable alkali-activated materials (AAMs) for soil stabilization because of their strong bonding capabilities. However, the influence of freeze-thaw cycles (FTCs) on the performance of geopolymer-stabilized soils reinforced with fibers remains largely unexplored. In the current study, for the first time, the durability of polypropylene fiber (PPF) reinforced clayey soil stabilized with fly ash (FA) based geopolymer is investigated under FTCs, evaluating its performance during prolonged seasonal freezing. The effects of repeated FTCs (0, 1, 3, 6, and 12 cycles), different contents of alkali-activated FA (5 %, 10 %, and 15 %), varying PPF percentages (0 %, 0.4 %, 0.8 %, and 1.2 % with a length of 6 mm), and curing time (7 and 28 days) on the properties of stabilized samples have been determined through tests including standard Proctor compaction, unconfined compressive strength (UCS), mass loss, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), and Fourier transform infrared spectroscopy (FTIR). The results revealed that a 0.4 % PPF concentration maximized strength in FA-based geopolymer samples by restricting crack propagation, irrespective of FA content, number of FTCs, or curing time. However, higher PPF contents lowered UCS values and Young's modulus due to fiber clustering and increased failure strain, respectively. Generally, an initial increase in UCS, Young's modulus, and resilience modulus (MR) of stabilized samples occurred with more FTCs because of their dense structure, delayed pore formation, and continued geopolymerization process and followed by a constant or decreasing trend in strength after 6 (or 3 in some cases) FTCs due to ice expansion in created air voids. Longer curing time resulted in denser samples with improved resistance to FTCs, especially under 12 FTCs. Moreover, samples with 10 % alkali-activated FA demonstrated the least susceptibility to FTCs. While initial FTCs caused no mass loss, subsequent cycles led to increased mass loss and remained below 2 % for all samples. Microstructural analysis results corroborated UCS test results. Although the primary chemical composition remained unchanged after 12 FTCs, these cycles induced morphological changes such as critical void formation and cracking within the gel structure. The stabilization approach proposed in this study demonstrated sustained UCS after 12 FTCs, promising reduced maintenance costs and extended service life in regions with prevalent freeze-thaw damage.

This research compares the stabilization efficiency of kaolinite and montmorillonite clayey soils using two industrial and agricultural by-products, namely fly ash (FA) and rice husk ash (RHA), activated by sodium hydroxide (NaOH). To this end, various proportions of FA and RHA (i.e., 0%, 5%, 10%, 15%, and 20%), along with NaOH solutions at 2 M and 4 M concentrations, are utilized to treat both low-and high-plasticity clayey soils. The resulting geopolymers are then subjected to a wide range of mechanical and micro-structural tests, including standard compaction, unconfined compressive strength (UCS), ultrasonic pulse velocity (UPV), swelling potential, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR). Results show that incorporating both FA and RHA into kaolinite and montmorillonite clays up to their respective optimal contents significantly enhances all their mechanical properties. However, FA-based geopolymers exhibit superior mechanical properties compared to RHA-based ones under similar additive contents and curing conditions. Accordingly, the optimal FA content is found to be 15%, while for the RHA-based geopolymers, the peak UCS is observed at 15% and 10% RHA for kaolinite and 10% and 5% RHA for montmorillonite when treated with 2 M and 4 M NaOH solutions, respectively. The results also suggest that FA is more effective than RHA in controlling the swelling potential of both kaolinite and montmorillonite soils. Microstructural analyses further corroborate the findings of macro-scale experiments by showcasing the comparative occurrence of geopolymerization, as well as the formation of cementitious gels, and synthesis of new chemical products.

The purpose of this study was to evaluate the sustainability benefits of Class F fly ash (FA), lime sludge (LS), and ground granulated blast furnace slag (GGBS)-based geopolymer-stabilized Edgar plastic kaolin (EPK) clay using the sustainability index (ISus) approach. Geotechnical engineering operations usually precede most infrastructural projects, making pavement construction an integral contributor to various environmental effects, due to the production of enormous quantities of greenhouse gas emissions through soil stabilization activities. To nip these concerns in the bud, effective integration of these environmental implications must be achieved during the geotechnical planning phase. The life cycle assessment (LCA) method was used to assess a wide range of environmental effects of a project, from raw material procurement, manufacturing, transportation, construction, and maintenance to final disposal. It is a well-recognized tool for designing environmentally sustainable projects. Experimental results from the geopolymer-stabilized EPK clay showed a notable improvement in unconfined compressive strength of the geopolymer-stabilized clay with 15% (FA + LS) and 5% (FA + GGBS) contents of up to 697% and 464%, respectively, after 28 days of curing at elevated temperature, 70 degrees C. The sustainability index (ISus) of geopolymer and lime treatment methods was analyzed based on the concept of environmental, resource consumption, and socioeconomic concerns, which quantifies the sustainability through greenhouse gas emission, environmental impacts, and the cost of utilizing FA, LS, and GGBS in soil stabilization compared with traditional lime. LCA was conducted for traditional lime treatment, FA-LS, and FA-GGBS geopolymer-stabilized subgrades to determine the most sustainable treatment method. From the sustainability analysis, using FA, LS, and GGBS as geopolymer stabilizers for kaolin clay reduced the global warming potential by 98.03% and 77.55% over the traditional lime stabilizers at 8% dosage. More importantly, results from the sustainability index (ISus) computations showed that FA-LS (ISus = 12.88) and FA-GGBS (ISus = 29.72) geopolymer treatment methods of EPK clay subgrade soils are more sustainable alternatives compared to the traditional lime (ISus = 48.07) treatment method.