The impact of the field conditions on needle-punched mulches made of cellulose fibres and PLA biopolymer during the 300 days of exposure was investigated. The study observed the degradation of nonwoven mulches during specific exposure periods (30, 90, 180 and 300 days), evaluating their mechanical, morphological and chemical properties. The impact of nonwoven mulches on soil temperature and moisture, consequently on the number of microorganisms developed beneath mulches after 300 days of exposure, were analysed and associated with obtained results complementing comprehension of nonwoven mulch degradation. The findings show that nonwoven mulches made from jute, hemp, viscose and PLA fibres change when exposed to environmental conditions (soil, sunlight, rainfall, snow, ice accumulation, air and soil temperatures, wind). The changes include alterations in colour, structure shifts and modifications in properties. The results highlight the degradation pathways of cellulose and PLA mulches, revealing that cellulose-based fibres degrade through the removal of amorphous components, leading to increased crystallinity and eventual structural breakdown. WAXD findings demonstrated that microbial and environmental factors initially enhance crystalline regions in cellulose fibres but ultimately reduce tensile strength and flexibility due to amorphous phase loss. FTIR analysis confirmed the molecular changes in cellulose chains, particularly in pectin and lignin, while SEM provided direct evidence of surface damage and fibre disintegration. Furthermore, it was found that fibre types of nonwoven mulch influence soil moisture retention and soil microbial activity due to a complex interplay of fibre composition, environmental conditions and nonwoven fabric characteristics. Comprehensive mechanical, morphological and chemical results of different types of nonwoven mulch during the 300 days of exposure to the field conditions provide valuable insights into sustainable practices for using nonwoven mulches for growing crops.