The large amount of slag generated during the construction of earth pressure balance shield (EPBS) not only incurs significant disposal costs, but also exacerbates environmental pollution. To improve the utilization of the shield slag, silty clay with additive is proposed as a slag conditioner instead of bentonite. Firstly, various macroscopic properties of the bentonite and silty clay slurries are tested. Subsequently, the relationships between the macroscopic properties of the silty clay slurries containing additives and the modification mechanism are evaluated at microscopic, mesoscopic, and macroscopic scales by using infrared spectroscopy (IR), scanning electron microscope (SEM), and Zeta potential tests, respectively. Based on these tests, reasons for variations in modification effects of different slurries are identified. The results show that addition of 3 % sodium carbonate to the silty clay can effectively improve the rheological properties of the slurry. The modification mechanism of sodium carbonate involves the formation of hydrogen bonds between water molecules and inner surface hydroxyl groups within the lattice layer of kaolinite. This process significantly enhances the rheological properties of the silty clay slurry. Furthermore, sodium carbonate alters the contact relationships between the silty clay particles, which increases viscosity and reduces permeability of the slurry. Finally, sodium carbonate increases thickness of the electrical double layer of the silty clay particles. This allows the particles to bind more water molecules, therefore improving slurry-making capacity of the silty clay. This paper presents an innovative multiscale analysis of the modification process of silty clay. The substitution of recycled silty clay for bentonite as a slag conditioner not only substantially reduces the cost of purchasing materials, but also considerably decreases the expenses associated with transportation and disposal of the soil discharged by EPBS.

Land reclamation from the sea is increasingly common in coastal areas in China as its urban population continues to grow and the construction of subways in these areas becomes an effective way to alleviate transportation problems. Earth pressure balance shield (EPBS) tunneling in reclaimed lands often faces the problem of seawater erosion which can significantly affect the effectiveness of soil conditioning. To investigate the impacts, in this work, the stratum adaptability of EPBS foaming agents in seawater environments was evaluated based on a series of laboratory tests. The Atterberg limits and vane shear tests were carried out to understand the evolution characteristics of mechanical properties of clay-rich soils soaked in seawater and then conditioned with foams. The results revealed that, for the same foaming agents, the liquid limit and plastic limit of soils soaked in seawater were lower than those in deionized water due to the thinning of bound water films adsorbed on the surface of soil particles. Similarly, soils soaked in seawater had lower shear strength. In addition, the results indicated that the foam volume (FV) produced by foaming agents using seawater as the solvent was slightly higher than that when using the deionized water due to the higher hydration capacity of inorganic salt cations in seawater compared with organic substances. It was also shown that seawater had negative effects on the half-life time (T1/2) and the dynamic viscosity (eta) of foaming agents due to the neutralization reaction between anions in the foaming agents and Na+ present in seawater. The test results also confirmed that 0.5 % of the tackifier (CMC) can alleviate the issue of thin foam films caused by seawater intrusion and improve the dynamic viscosity of foaming agents more effectively, leading to superior resistance to seawater intrusion in EPBS tunnel constructions.