In food packaging industry, plastic was the most commonly used material for packaging, which caused serious pollution to the marine and soil environment. The researches on biodegradable films development from biodegradable polymers was arise, which was expected to ensure the quality and safety of food as much as possible. Biodegradable materials for films included polysaccharides and proteins of different biological sources, and synthetic materials. This review discussed the molecular characteristics and film-forming properties of natural polymer materials of polysaccharides from halobios, plant and microorganism, protein from animal, plant, milk. In addition, the effects of polymerization degree, crystallinity, and film-forming process of synthetic materials (polycaprolactone, polyvinyl alcohol, polylactic acid) on film performance was studied. In order to improve the practicality of biodegradable films in food packaging, many methods were explored to enhance the physical performance of the films. The enhancement strategies including: introduction of nanoparticles, chemical modification, and blending with other polymers, which can effectively enhance the mechanical properties and water vapor barrier performance of biodegradable films. Furthermore, it will provide a reference for future research interest that to development biodegradable food packaging films with high mechanical and barrier properties.

To enhance the barrier performance of biomass films, carboxymethyl cellulose (CMC) was combined with montmorillonite (MMT) modified by stearyltrimethylammonium bromide (STAB) and loaded with Fe3O4 particles as a nano-filler, and a CMC/m-OMMT mulch film was fabricated using magnetic field orientation. The characterization of m-OMMT was conducted through Fourier-transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), and vibrating sample magnetometry (VSM), which confirmed the successful intercalation of STAB into the MMT structure, along with the effective loading of Fe3O4 particles onto the MMT matrix. A comprehensive investigation into the mechanical properties of CMC/m-OMMT films revealed that, in the dry state, the films exhibited a tensile strength of 29 MPa and an elongation at break of 64 %. A series of barrier performance tests were conducted on the films. The findings demonstrated that the incorporation of MMT and the application of a magnetic field substantially enhanced the water contact angle, increasing it from 86 degrees to 112 degrees. Additionally, water vapor permeability increased by approximately 30 %, soil erosion was reduced by about 22 %, and UV resistance was notably improved by 94 %. Moreover, scanning electron microscopy (SEM), thermogravimetric analysis (TGA), and biodegradation tests on the CMC/m-OMMT/40mT films revealed that the magnetic field effectively oriented the MMT nanosheets within the composite matrix. This study presents a novel approach for enhancing the barrier properties of biomass-based mulch films.

Although poly (lactic acid) (PLA) is a good environmentally-friendly bio-degradable polymer which is used to substitute traditional petrochemical-based polymer packaging films, the barrier properties of PLA films are still insufficient for high-barrier packaging applications. In this study, oxygen scavenger hydroxyl-terminated polybutadiene (HTPB) and cobalt salt catalyst were incorporated into the PLA/poly (butylene adipate-co-terephthalate) (PLA/PBAT), followed by melting extrusion and three-layer co-extrusion blown film process to prepare the composite films. The oxygen permeability coefficient of the composite film combined with 6 wt% oxygen scavenger and 0.4 wt% catalyst was decreased significantly from 377.00 cc mil m-2 day-1 0.1 MPa-1 to 0.98 cc mil m-2 day-1 0.1 MPa-1, showing a remarkable enhancement of 384.69 times compared with the PLA/PBAT composite film. Meanwhile, the degradation behavior of the composite film was also accelerated, exhibiting a mass loss of nearly 60% of the original mass after seven days of degradation in an alkaline environment, whereas PLA/PBAT composite film only showed a mass loss of 32%. This work has successfully prepared PLA/PBAT composite films with simultaneously improved oxygen barrier property and degradation behavior, which has great potential for high-demanding green chemistry packaging industries, including food, agricultural, and military packaging. (c) 2024 Institute of Process Engineering, Chinese Academy of Sciences. Publishing services by Elsevier B.V. on behalf of KeAi Communications Co., Ltd. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).

In this study, the base film (CSL) was prepared by blending tunicate cellulose nanocrystals (TCNCs) extracted from tunicate shells, with sodium alginate (SA) and alkali lignin (AL). Then, the mulching film (CSL-WK) was prepared using water-borne polyurethane (WPU) as binder to install low-energy Kaolin on the surface of CSL film. The influences of composition with different concentrations on mechanical properties were studied. The tensile strength and elongation at break of CSL-WK film could reach 86.58 MPa and 50.49 %, respectively. The mulching films were characterized by degradability test, SEM, FTIR, and TGA. TCNCs had good compatibility with SA and AL, and a rough structure was formed on the surface of the film to improve the hydrophobicity. The barrier properties, including ultraviolet resistance, water contact angle, water vapor permeability, water retention, and flame retardancy, were tested. The results showed that CSL-WK films could block 97 % of ultraviolet light, reduce about 25 % of soil water loss, and self-extinguish within 7 s of open flame ignition. Note that the secondary spraying method significantly improved the barrier property of films. This study lays a foundation for the preparation of ecologically friendly, biodegradable, and high barrier mulching film, and expands the application of marine resources.