Sodium hydroxide (NaOH)-sodium silicate-GGBS (ground granulated blast furnace slag) effectively stabilises sulfate-bearing soils by controlling swelling and enhancing strength. However, its dynamic behaviour under cyclic loading remains poorly understood. This study employed GGBS activated by sodium silicate and sodium hydroxide to stabilise sulfate-bearing soils. The dynamic mechanical properties, mineralogy, and microstructure were investigated. The results showed that the permanent strain (epsilon(p)) of sodium hydroxide-sodium silicate-GGBS-stabilised soil, with a ratio of sodium silicate to GGBS ranging from 1:9 to 3:7 after soaking (0.74%-1.3%), was lower than that of soil stabilised with cement after soaking (2.06%). The resilient modulus (E-d) and energy dissipation (W) of sodium hydroxide-sodium silicate-GGBS-stabilised soil did not change as the ratio of sodium silicate to GGBS increased. Compared to cement (E-d = 2.58 MPa, W = 19.96 kJ/m(3)), sulfate-bearing soil stabilised with sodium hydroxide-sodium silicate-GGBS exhibited better E-d (4.84 MPa) and lower W (15.93 kJ/m(3)) at a ratio of sodium silicate to GGBS of 2:8. Ettringite was absent in sodium hydroxide-sodium silicate-GGBS-stabilised soils but dominated pore spaces in cement-stabilised soil after soaking. Microscopic defects caused by soil swelling were observed through microscopic analysis, which had a significant negative impact on the dynamic mechanical properties of sulfate-bearing soils. This affected the application of sulfate-bearing soil in geotechnical engineering.

来源平台：PROCEEDINGS OF THE INSTITUTION OF CIVIL ENGINEERS-CONSTRUCTION MATERIALS