Mulching films serve various functions, such as temperature regulation, moisture retention, and weed suppression. They can substantially increase crop yields and are widely adopted in agricultural practices. However, the use of traditional plastic mulch films is limited by their difficult recycling processes and poor biodegradability, leading to soil contamination and negatively affecting crop growth. Consequently, eco-friendly alternatives are gaining attention as replacements for conventional petroleum-based films in agricultural applications. Enhancing the performance of these eco-friendly films remains a crucial challenge. Traditional polyvinyl alcohol (PVA) films have inherent limitations, including low mechanical strength and poor water resistance. In this work, a PVA/sodium alginate (SA)/glycerol (GLY)/glutaraldehyde (GA) film was prepared that is biodegradable, demonstrates superior mechanical properties, and offers exceptional transparency through glutaraldehyde crosslinking. The impact of GA on films was examined using characterization techniques. The findings revealed that the composite film has a uniform, compact surface with no observable holes or aggregation. The mechanical performance and water vapor barrier properties (WVP) of the film were significantly enhanced after GA crosslinking. The tensile strength and elongation at the break of the PVA/SA/GLY/GA film reached 33.73 MPa and 362.89%, respectively. This work offers a straightforward approach to the development of sustainable agricultural materials.

来源平台：JOURNAL OF APPLIED POLYMER SCIENCE