This paper investigated the influence of chloride ion erosion and aftershocks on the seismic performance of transmission tower structures in Xinjiang, China. Based on chloride ion diffusion laws and steel corrosion mechanisms, the time-dependent deterioration of reinforced concrete was analyzed. Finite element models considering corrosion effects were established for different ages(0a,50a,70a,100a) in a saline soil environment using ANSYS/LS-DYNA. Ten mainshock-aftershock sequences tailored to the site type was constructed, and the cumulative damage index (DI) was adopted as a metric for structural damage. The results indicate that aftershocks and steel corrosion significantly impact transmission tower damage, with damage extent influenced by the intensity of the main shock. Stronger aftershocks cause greater additional damage, potentially exceeding 50 % cumulative damage when their amplitude matches the main shock. Steel corrosion alone can lead to nearly 40 % damage. Its influence on seismic fragility varies with damage state, especially under moderate to complete damage, where longer service life increases vulnerability. The coupling of corrosion and aftershocks further elevates structural vulnerability. Hence, in seismic assessments of transmission towers in saline soil environments, combined effects of main and aftershocks, and corrosion, must be accounted for.